Detailed size range
General specifications:
According to the standard of wear-resistant brass rods, the diameter (or distance across the flats) of C24000 ranges from 5 to 80 mm, and the length ranges from 500 to 6000 mm, which is suitable for cross-sectional shapes such as round, hexagonal, and rectangular.
The hot extrusion (M30) specifications of conductive copper rods are 10 to 90 mm, and the drawing (H50) and annealing (060) specifications can be as low as 3 to 80 mm.
The specification range of extruded rods is wider, for example, the diameter of H62 brass round rods can reach 10 to 260 mm, and C24000 may be similar.
Special applications:
The diameter of copper rods for mineral insulated cables is 3 to 80 mm, and the cut length is required to be at least 20 m, with an allowable deviation of ±0.20 mm.
International Standards
The standardized specifications of C24000 involve multiple international and domestic standards:
Chinese Standards:
GB/T 5231-2012/2022: Its corresponding grade is listed as H80.
YS/T 649-2018: Covers the technical requirements for copper and copper alloy extruded rods.
International Standards:
ASTM: C24000 complies with American ASTM standards, such as ASTM B36 (General Standard for Brass Plates, Strips, and Rods).
ISO and JIS: Some products are marked as complying with ISO or Japanese JIS standards.
Main ingredients:
Copper (Cu): 78.5%-81.5% (Chinese standard GB/T 5231-2012), US UNS C24000 standard is 76%-80%
Zinc (Zn): Balance, about 18%-23.5%.
Impurity control:
Lead (Pb): Chinese standard requires ≤0.03% or ≤0.05%, while UNS C24000 contains 0.5% Pb (low-lead brass).
Iron (Fe): ≤0.05%-0.10%.
Phosphorus (P): ≤0.01%.
The total of other impurities is ≤0.3%.
Mechanical properties
Strength and plasticity:
Tensile strength: 360 MPa (52,000 psi), some data show lower (235 MPa), which may be related to different processing conditions (such as annealed or cold-processed).
Yield strength: 170 MPa (25,000 psi).
Elongation: 42% (50 mm gauge length), the plasticity of Chinese standard H80 is good, suitable for hot and cold pressure processing.
Elastic modulus:
117 GPa (17,000 ksi)
Hardness:
Brinell hardness 82 HB, relatively low, but can be improved by cold hardening.
Q1:Do you provide samples? Is it free or extra?
A1:Yes, we can provide samples free of charge and the customer will pay the freight.
Q2:What if I don't have export experience ?
A2:We have reliable forwarder agent which can ship items to you by sea/air/Express to your doorstep. Any way, we will help you choose the most suitable shipping service.
Q3:How long is your lead time?
A3:If it is in stock, it is usually 5-10 days. Or, if there is no inventory, 15 days, depending on the quantity.
Q4:What are your terms of payment?
A4:30% T/T deposit in advance, 70% T/T balance within 5 days after B/L copy, 100%.Irrevocable L/C at sight, 100% Irrevocable L/C after receive B/L 30-120 days, O/A.
Q5:How is your technical support?
A5:We provide lifetime online support through Whatsapp/ Skype/ Wechat/ Email. Any problem after delivery, we will offer you call anytime.